Authors: Wenqing Wang, Shu‐ang He, Zhe Cui, Qian Liu, Muk Fung Yuen, Jinqi Zhu, Hao Wang, Mengluan Gao, Wei Luo, Junqing Hu, Rujia Zou
Published: 2022-09-09
Source: Full article
AbstractThe poor conductivity, inert charge transmission efficiency, and irreversible Na+ trapping of Na2Ti3O7 result in retardant electrons/ions transportation and deficient sodium‐ion storage efficiency, leading to sluggish reaction kinetics. To address these issues, an urchin‐like Ti2CTx/Na2Ti3O7 (Ti2C/NTO) heterostructure sphere consisting of Ti2C/NTO heterostructure nanobelts array is developed via a facile one‐step in situ hydrothermal strategy. The Ti2C/NTO heterostructure can obviously decrease Na+ diffusion barriers and increase electronic conductivity to improve reaction kinetics due to the built‐in electric field effect and high‐quantity interface region. In addition, the urchin‐like vertically aligned nanobelts can reduce the diffusion distance of electrons and ions, provide favored electrolyte infiltration, adapt large volume expansion, and mitigate the aggregation to maintain structural stability during cycles, further enhancing the reaction kinetics. Furthermore, the Ti2C/NTO heterostructure can effectively suppress many unwanted side reactions between reactive surface sites of NTO and electrolyte as well as irreversible trapping of Na+. As a result, systematic electrochemical investigations demonstrate that the Ti2C/NTO heterostructure as an anode material for record sodium‐ion storage delivers the highest reversible capacity, the best cycling stability with 0.0065% decay rate for 4500 cycles at 2.0 A g–1, and excellent rate capability of 172.1 mAh g–1 at 10.0 A g–1.